产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-792 | | 1.42 | |
| 物理性能 | 吸水量 | 浸泡均衡点+73℉(+23℃) | ASTM D-570 | 1.40 | % |
| 吸水量 | 24hrs浸泡+73℉(+23℃) | ASTM D-570 | 0.32 | % | |
| 机械性能 | 弯曲疲劳忍耐限度 | +73℉ | ASTM D-671 | 4.0 | MPsi |
| 扩散因数 | +73℉(+23℃)106Hz | ASTM D-150 | 0.005 | | |
| 伸张强度 | +250℉ | ASTM D-638 | 3.3 | MPsi | |
| 断裂时之拉力伸张度 | +250℉(+122℃) | ASTM D-638 | >260 | % | |
| 伸张强度 | +122℃ | ASTM D-638 | 22.8 | MPa | |
| 弯曲疲劳忍耐限度 | +23℃ | ASTM D-671 | 27.6 | MPa | |
| 压缩应力 | +73℉@1%Def. | ASTM D-695 | 4.5 | MPsi | |
| 伸张强度 | +158℉ | ASTM D-638 | 6.6 | MPsi | |
| 压缩应力 | +23℃@10%Def. | ASTM D-695 | 108 | MPa | |
| 吸水量 | Equil.50%R.h.+73℉(+23℃) | ASTM D-570 | 0.28 | % | |
| 弯曲降服强度 | +73℉ | ASTM D-790 | 13.6 | MPsi | |
| 挠曲系数 | +73℉ | 在25℃下 | 400 | MPsi | |
| IZOD冲击强度 | +23℃ | ASTM D-256 | 69.4 | j/m | |
| 伸张强度 | +70℃ | ASTM D-638 | 45.5 | MPa | |
| IZOD冲击强度 | 40℃ | ASTM D-256 | 53.4 | j/m | |
| 伸张强度 | +23℃ | ASTM D-638 | 66.9 | MPa | |
| 伸张强度 | +212℉ | ASTM D-638 | 4.3 | MPsi | |
| 弹性系数 | +23℃ | ASTM D-638 | 3100 | MPa | |
| 挠曲系数 | +212℉ | 在25℃下 | 130 | MPsi | |
| 伸张强度 | +73℉ | ASTM D-638 | 9.7 | MPsi | |
| 挠曲系数 | +23℃ | 在25℃下 | 2760 | MPa | |
| 伸张强度 | -68℉ | ASTM D-638 | 14.0 | MPsi | |
| 断裂时之拉力伸张度 | +212℉(+100℃) | ASTM D-638 | >260 | % | |
| 弹性系数 | +73℉ | ASTM D-638 | 450 | MPsi | |
| 伸张强度 | -55℃ | ASTM D-638 | 96.5 | MPa | |
| 剪力 | +23℃ | ASTM D-732 | 65.5 | MPa | |
| 挠曲系数 | +70℃ | 在25℃下 | 1515 | MPa | |
| 伸张强度 | +100℃ | ASTM D-638 | 29.6 | MPa | |
| 挠曲系数 | +158℉ | 在25℃下 | 220 | MPsi | |
| 断裂时之拉力伸张度 | +73℉(+23℃) | ASTM D-638 | 25 | % | |
| 挠曲系数 | -55℃ | 在25℃下 | 3930 | MPa | |
| 压缩应力 | +73℉@10%Def. | ASTM D-695 | 15.6 | MPsi | |
| 挠曲系数 | -68℉ | 在25℃下 | 570 | MPsi | |
| 压缩应力 | +23℃@1%Def. | ASTM D-695 | 31.0 | MPa | |
| 摩擦系数 | +73℉(+23℃)动态 | ThrustWasherTest3 | 0.20 | | |
| 负载下之变形 | 2000psi@+122℉(14Mpa@50℃) | ASTM D-621 | 0.7 | % | |
| 剪力 | +73℉ | ASTM D-732 | 9.5 | MPsi | |
| IZOD冲击强度 | -40℉ | ASTM D-256 | 1.0 | ft.lb/in | |
| 弯曲降服强度 | +23℃ | ASTM D-790 | 93.8 | MPa | |
| 挠曲系数 | +100℃ | 在25℃下 | 895 | MPa | |
| 挠曲系数 | +122℃ | 在25℃下 | 550 | MPa | |
| 断裂时之拉力伸张度 | +158℉(+70℃) | ASTM D-638 | 150 | % | |
| IZOD冲击强度 | +73℉ | ASTM D-256 | 1.3 | ft.lb/in | |
| 电气性能 | 绝缘强度 | Short Time,2.3mm | ASTM D-149 | 19.7 | MV/m |
| 电阻系数 | +73℉(+23℃)0.2%H2O | ASTM D-257 | 1015 | ohm-cm | |
| 绝缘系数 | +73℉(+23℃)102to106Hz | ASTM D-150 | 3.7 | | |
| 电弧 | 120mil(3.1mm) | ASTM D-495 | 220no tracking | Sec. | |
| 绝缘强度 | Short Time,90 mils | ASTM D-149 | 500 | V/mil | |
| 热性能 | 线性热膨胀系数 | +220 to +300℉ | ASTM D-696 | 8.3 | 10-5in/in.℉ |
| 线性热膨胀系数 | +140 to +220℉ | ASTM D-696 | 7.6 | 10-5in/in.℉ | |
| 热变形温度 | 0.5MPa | ASTM D-648 | 170 | ℃ | |
| 热变形温度 | 1.8MPa | ASTM D-648 | 130 | ℃ | |
| 线性热膨胀系数 | +60 to +104℃ | ASTM D-696 | 13.7 | 10-5m/m.℃ | |
| 熔点 | | ASTM D-2133 | 347 | ℉ | |
| 线性热膨胀系数 | +29 to +60℃ | ASTM D-696 | 12.2 | 10-5m/m.℃ | |
| 线性热膨胀系数 | -40 to +85℉ | ASTM D-696 | 5.8 | 10-5in/in.℉ | |
| 可燃烧性 | | UL-94 | 94HB | | |
| 熔点 | ASTM D-2133 | | 175 | ℃ | |
| 热变形温度 | 66psi | ASTM D-648 | 328 | ℉ | |
| 线性热膨胀系数 | +104 to +150℃ | ASTM D-696 | 14.9 | 10-5m/m.℃ | |
| 线性热膨胀系数 | -40 to +29℃ | ASTM D-696 | 10.4 | 10-5m/m.℃ | |
| 热变形温度 | 264psi | ASTM D-648 | 266 | ℉ | |
| 线性热膨胀系数 | +85 to +140℉ | ASTM D-696 | 6.8 | 10-5in/in.℉ | |
（1） POM加工前可不用干燥,*在加工过程中进行预热(80℃左右),对产品尺寸的稳定性有好处.
（2） POM的加工温度很窄(0～215℃),在炮筒内停留时间稍长或温度超过220℃时就会分解,产生刺激性强的甲醛气体.
（3） POM料注塑时保压压力要较大(与注射压力相近),以减少压力降.螺杆转速不能过高,残量要少;
（4） POM产品收缩率较大,易产生缩水或变形.POM比热大,模温高(80～100℃),产品脱模时很烫,需防止手指.
（5） POM宜在“中压、中速、低料温、较高模温”的条件下成型加工,精密制品成型时需用控制模温
（6） 具高机械强度和刚性
（7） *的疲劳强度
（8） 环境抵抗性、耐有机溶剂性佳
（9） 耐反覆冲击性强,良好的电气性质,复原性良好,具自已润滑性、耐磨性良好,尺寸安定性优库存图