| 性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
| 机械性能 | 拉伸强度(引张强度) |
|
ASTM D638/ISO 527 |
|
kg/cm2(MPa)[Lb/in2] |
| 断裂伸长率 |
|
ASTM D638/ISO 527 | >50 | % | |
| 拉伸模量 |
|
ASTM D638/ISO 527 | 2400 | kg/cm2(MPa)[Lb/in2] | |
| 拉伸屈服伸长率(延伸率) |
|
ASTM D638/ISO 527 |
|
% | |
| 拉伸断裂伸长率(延伸率) |
|
ASTM D638/ISO 527 |
|
% | |
| 弯曲模量(弯曲弹性率) |
|
ASTM D790/ISO 178 | 2400 | kg/cm2(MPa)[Lb/in2] | |
| 弯曲强度 |
|
ASTM D790/ISO 178 | 97 | kg/cm2(MPa)[Lb/in2] | |
| 洛氏硬度 |
|
ASTM D785 |
|
|
|
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | |
| 1/4" -30℃ | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" 23℃ | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" -30℃ | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| Charpy冲击强度 | 23℃ （缺口） | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | |
| -30℃（缺口） | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| 23℃（无缺口） | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（无缺口） | ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in | ||
| 物性性能 | 比重（密度） |
|
ASTM D792/ISO 1183 | 1.2 |
|
| 成型收缩率 |
|
ASTM D955 | 0.6-0.8 | % | |
| 熔融指数（流动系数） | 200℃/5kg | ASTM D1238/ISO 1133 |
|
g/10min | |
| 220℃/10kg | ASTM D1238/ISO 1133 |
|
g/10min | ||
| 吸水率 23℃/24H |
|
ASTM D570/ISO 62 | 0.12-0.3 | % | |
| 热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 |
|
℃（℉） |
| 未退火 | ASTM D648/ISO 75 |
|
℃（℉） | ||
| 维卡软化点 |
|
ASTM D1525/ISO R306 | 145 | ℃（℉） | |
| 熔点 |
|
- |
|
℃（℉） | |
| 燃烧性（率） |
|
UL94 |
|
|
|
| 线性膨胀系数 |
|
ASTM D696/ISO 11359 |
|
mm/mm.℃ | |
| 电气性能 | 介电常数 | 100HZ | ASTM D150/IEC 60250 |
|
|
| 1MHZ | ASTM D150/IEC 60250 |
|
|
||
| 介电损耗 | 100HZ | ASTM D150/IEC 60250 |
|
|
|
| 1MHZ | ASTM D150/IEC 60250 |
|
|
||
| 体积电阻率 |
|
ASTM D257/IEC 60093 |
|
Ω.cm | |
| 表面电阻率 |
|
ASTM D257/IEC 60093 |
|
Ω | |
| 耐电弧性 |
|
ASTM D495/IEC 60112 |
|
|
|
| 光学性能 | 折射率 |
|
ASTM D542/ISO 489 | 1.586 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|