| 规格级别 | 其它 其它 脱模 | 外观颜色 |
|
|---|---|---|---|
|
|
|
||
|
|
|
||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
|
物理性能 |
比重 |
|
ASTM D792 | 1.14 | g/cm3 |
| 熔流率 | 330℃/2.16kg | ASTM D1238 | 8.0 | g/10min | |
| 吸水率 | 饱和 | ASTM D570 | 0.30 | % | |
| 平衡 | ASTM D570 | 0.12 | % | ||
|
机械性能 |
拉伸模量 |
|
ASTM D638 | 2400 | MPa |
| 抗张强度 | 屈服 | ASTM D638 | 75.8 | MPa | |
| 断裂伸长率 |
|
ASTM D638 | >50 | % | |
| 热性能 | 热变形温度 | 0.45MPa | ASTM D648 | 192 | ℃ |
| 1.8MPa | ASTM D648 | 175 | ℃ | ||
| 维卡软化温度 |
|
ISO 306/B120 | 203 | ℃ | |
| 线形膨胀系数 | 流动 | ASTM D696 | 0.000070 | cm/cm/℃ | |
| 横向 | ASTM D696 | 0.000070 | cm/cm/℃ | ||
| UL 阻燃等级 | 1.50mm | UL 94 | HB |
|
|
| 灼热丝易燃指数 | 2.00mm | IEC 60695-2-12 | 800 | ℃ | |
| 极限氧指数 |
|
ISO 4589-2 | 25 | % | |
| 电气性能 | 表面电阻率 |
|
ASTM D257 | ＞1.0E+16 | ohms |
| 体积电阻率 | 23℃ | ASTM D257 | ＞1.0E+15 | ohm·m | |
| 介电强度 |
|
ASTM D149 | 35 | KV/mm | |
| 介电常数 | 60Hz | ASTM D150 | 3.00 |
|
|
| 1MHz | ASTM D150 | 2.90 |
|
||
| 耗散因数 | 60Hz | ASTM D150 | 0.0010 |
|
|
| 1MHz | ASTM D150 | 0.010 |
|
||
| 其他性能 | UL 阻燃性能 | 1.50 mm | UL94 | HB |
|
| 3.00 mm | UL94 | HB |
|
||
| 极限氧指数 |
|
ASTM D2863 | 24 | % | |
由于原材料浮动比较大，我们的每一款产品价格无法十分 地展示在客户面前，因此我们也只是标出一个象征性的价格，如果您对我们的产品非常感兴趣，请联系我们，我们将尽快给您报价。
本厂产品材料规格基本是按客户要求定做的，加上原材料价格会有浮动，所以成品价格会有不同。展示的产品只是列举了一些样品，订货前请务必咨询我们修改价格，或者直接致电我们！
PC是几乎无色的玻璃态的无定形聚合物，有很好的光学性。PC高分子量树脂有很高的韧性，悬臂梁缺口冲击强度为600~900J/m，未填充牌号的热变形温度大约为130°C，玻璃纤维增强后可使这个数值增加10°C。PC的弯曲模量可达2400MPa以上，树脂可加工制成大的刚性制品。低于100°C时，在负载下的蠕变率很低。